Photoelectrochemically Self-Improving Si/GaN Photocathode - Data and Resources
| Project ID | df421bd8-bc26-449c-a750-428cfb2cb69c |
|---|---|
| Dataset ID | 1e218b97-fd36-47a9-90d4-73f172e0fccd |
Data and Resources
-
fig1a_raw_data.xlsxXLSX
Data API
Chronoamperometry (CA) testing of Si/GaN photocathode in 0.5M (pH=0.4)...
-
fig1b_raw_data.xlsxXLSX
Data API
Chronoamperometry (CA) testing of Si/GaN photocathode in 0.5M sulfuric acid...
-
fig1c_raw_data.xlsxXLSX
Intermittent chronoamperometry (CA) testing was performed on Si/GaN...
-
fig1d_raw_data.xlsxXLSX
Two Si/GaN photocathodes were compared. Sample #1 (named as S#1) was the...
-
fig2b_raw_data.xlsxXLSX
Data API
Photoconductive atomic force microscopy (PC-AFM) measurements were conducted...
-
fig2d_raw_data.xlsx.xlsx
Line scan extracting the topography and photocurrent from a 10 hours...
-
fig3c_raw_data.xlsx.xlsx
Surface chemical composition and valence band structure of GaN were obtained...
-
fig3d_raw_data.xlsx.xlsx
Data API
X-ray photoemission spectroscopy (XPS) O1s core level spectra from 1 hour...
-
fig3f_raw_data.xlsxXLSX
Data API
X-ray photoemission spectroscopy (XPS) O1s core level spectra from 10 hours...
-
fig3e_raw_data.xlsxXLSX
Data API
X-ray photoemission spectroscopy (XPS) O1s core level spectra from 4 hours...
-
fig4a_raw_data.xlsx.xlsx
The density-functional theory (DFT) calculations were performed with the...
-
fig4b_raw_data.xlsx.xlsx
Calculated formation energy of (101 ̅0) m-plane GaN surfaces with different...